Precipitation-hardening stainless steel 1.4594

Precipitation-hardening stainless steel 1.4594

1.4594 stainless steel equal material : SUS632 , UNS S15700 , X5CrNiMoCuNb14-5 , 15-7MO

PH1.4594 steel was at 2% Mo instead of 0Cr17Ni7Al steel in 2% chromium steels and development, the basic properties of 0Cr17Ni7Al steels with similar, but its good comprehensive properties than. PH1.4594 stainless steel can withstand all kinds of cold forming and welding process in the austenitic state, followed by heat treatment and can get the highest strength; PH1.4594o stainless steel has excellent high-temperature strength at 550 degree .

PH1.4594 stainless steel chemical composition:

	Cr	Mo	C	Mn	Si	Al	Ni	P	S
Min	14.0	2.0				0.75	6.5
Max	16.0	3.0	0.09	1.00	1.00	1.50	7.7	0.04	0.03

PH1.4594 stainless steel mechanical property:

Alloy	Tensile strength MPa	Yield strength MPa	elongation %
PH1.4594	520	205	40

PH1.4594 steel physical property:
Heat treatment specification: solution 1010 - 1150 degree fast cooling

PH1.4594 steel exciting form:
1.4594 stainless steel plate, 1.4594 stainless steel sheet, 1.4594 stainless steel bar, 1.4594 stainless steel wire, 1.4594 stainless steel tube, 1.4594 stainless steel forgings
PH1.4594 steel chief application:
Used in the manufacture of thin-walled structure components, containers, pipelines, spring, valve membrane, ship shaft, compressor disc,reactor components, as well as a variety of chemical equipment and other structural parts.