N08810

Product : N08810

N08810 Nickel base alloy for a face-centered cubic lattice structure. Very low carbon content and improving the Ti: C ratio increases the stability and structure of the largest anti-allergy activity and resistance to intergranular corrosion. Low temperature annealing around 950 ℃ guaranteed fine grain structure.

N08810 Nickel base alloy Chemical Composition %

Ni	Cr	Fe	C	Al	Ti
32.0	21.0	45.0	0.08	0.3	0.4

N08810 Nickel base alloy Mechanical properties

Alloy

Yield Strength

R P0.2N/mm2

Tensile strength

Rm N/mm2

Elongation

A5%

800

180

450

N08810 Nickel base alloy Physical properties

Density	8.0g/cm3
Melting point	1350-1400℃

N08810 Nickel base alloy corrosion :
N08810 resistant to many corrosive media corrosion. Its high nickel content in aqueous corrosion conditions has good resistance to stress corrosion cracking. High chromium content so that it has better resistance to pitting and crevice corrosion cracking. The alloy has good resistance to nitric acid, organic acid corrosion, but limited corrosion resistance in sulfuric acid and hydrochloric acid. In addition to pitting corrosion may occur halide, there are very good corrosion resistance in oxidizing and non-oxidizing salt. Water, steam and mixtures of steam, air, carbon dioxide also has good corrosion resistance.

N08810 Nickel base alloy Application field have :
1 . Condenser nitrate - nitric acid corrosion resistance
2 . Steam heating pipes - very good mechanical properties
3 . The heating element tube - very good mechanical properties