Nickel W.Nr 2.4068 alloy

Nickel W.Nr 2.4068 alloy
Nickel W.Nr 2.4068 alloy equal material :N02201, W.Nr 2.4061,W.Nr 2.4060, Nickel 201

Nickel W.Nr 2.4068 alloy as part of the malleability of industrial pure nickel. Pure nickel has goodmechanical properties can be excellent corrosion resistant performance. Pure nickel has good chemicaland magnetic properties.

Nickel W.Nr 2.4068 alloy Chemical composition:

Alloy	%	Ni	Fe	C	Mn	Si	Cu	S
NickelW.Nr2.4068	Min	Margin
NickelW.Nr2.4068	Max	Margin	0.4	0.02	0.35	0.35	0.25	0.01

Nickel W.Nr 2.4068 alloy Physical properties:
Nickel W.Nr 2.4068 alloy density:8.89 g/cm³
Nickel W.Nr 2.4068 alloy Melting point:1440 degree

Nickel W.Nr 2.4068 alloy mechanical properties at room temperature, the minimum value :

State	Condition	TensilestrengthRmN/mm2	Yieldstrength RP0.2N/mm2	Elongation A5%	HardnessHB
NickelW.Nr2.4068alloyroundbar	Hotrolled	60-85	15-45	35-55	45-80
NickelW.Nr2.4068alloyroundbar	Colddrawnorannealing	55-75	15-30	40-55	45-70
NickelW.Nr2.4068alloyplate	Annealing	55-80	15-40	40-60	45-75
NickelW.Nr2.4068alloySheet	Annealing	55-75	15-30	40-55	70max
NickelW.Nr2.4068alloyPipe	Seamlessannealing	55-75	12-30	40-60	70max

Nickel W.Nr 2.4068 Features:
Nickel200 is very low carbon content of the pure commercial nickel, has been approved for use in service is as high as 1230 degree high temperature environment.
Nickel W.Nr 2.4068 Application fields:
Food processing equipment, salt refining equipment.
Mining and ocean mining.
At above 300 degree under the condition of equipment needed for manufacturing industrial sodium hydroxide.
Organic or inorganic chloride and fluoride production: corrosion resistance to chlorine and fluorine

A nuclear reactor
Retort and parts heat treatment furnace, especially in the carbide and nitride atmosphere
Catalytic regenerator in petrochemical production is recommended to use in the application of above 700 degree alloy 600 to obtain a longer service life.