Nickel W.Nr 2.4060 alloy

Nickel W.Nr 2.4060 alloy
Nickel W.Nr 2.4060 alloy equal material :N02201, W.Nr 2.4068, W.Nr 2.4061,W.Nr 2.4060, Nickel 201

Nickel W.Nr 2.4060 alloy as part of the malleability of industrial pure nickel. Pure nickel has good mechanical properties can be excellent corrosion resistant performance. Pure nickel has good chemical and magnetic properties.

Nickel W.Nr 2.4060 alloy Chemical composition:

Alloy	%	Ni	Fe	C	Mn	Si	Cu	S
Nickel W.Nr 2.4060	Min	Margin
Nickel W.Nr 2.4060	Max	Margin	0.4	0.02	0.35	0.35	0.25	0.01

Nickel W.Nr 2.4060 alloy Physical properties:
Nickel W.Nr 2.4060 alloy density:8.89 g/cm³
Nickel W.Nr 2.4060 alloy Melting point:1440 degree

Nickel W.Nr 2.4060 alloy mechanical properties at room temperature, the minimum value :

State	Condition	Tensile strength Rm N/mm2	Yield strength RP 0.2 N/mm2	Elongation A5 %	Hardness HB
NickelW.Nr2.4060 alloy round bar	Hot rolled	60-85	15-45	35-55	45-80
NickelW.Nr2.4060 alloy round bar	Cold drawn or annealing	55-75	15-30	40-55	45-70
NickelW.Nr2.4060alloy plate	Annealing	55-80	15-40	40-60	45-75
Nickel W.Nr 2.4060 alloy Sheet	Annealing	55-75	15-30	40-55	70 max
Nickel W.Nr 2.4060 alloy Pipe	Seamless annealing	55-75	12-30	40-60	70 max

Nickel W.Nr 2.4060 Features:
Nickel W.Nr 2.4060 is very low carbon content of the pure commercial nickel, has been approved for use in service is as high as 1230 degree high temperature environment.

Nickel W.Nr 2.4060 Application fields:
Food processing equipment, salt refining equipment.

At above 300 degree under the condition of equipment needed for manufacturing industrial sodium hydroxide.
Organic or inorganic chloride and fluoride production: corrosion resistance to chlorine and fluorine

Retort and parts heat treatment furnace, especially in the carbide and nitride atmosphere
Catalytic regenerator in petrochemical production is recommended to use in the application of above 700 degree alloy 600 to obtain a longer service life.