B650L hot rolled coils

B650L steel for automobile beams have high strength and good bending performance, which is suitable for beam parts.

Grade	C	Si	Mn	p	S	Al	Nb	V	Ti
B650L	≤0.10	≤0..50	≤2.00	≤0.025	≤0.010	≥0.015	≤0.09	≤0.20	≤0.15

B650L steel Mechanical Properties

Grade	Yield strength (MPa)	Tensile strength (MPa)	Elongation (%)		180 degree cold bend, diameter
			Thickness＜3mm Lo=80mm, b=20mm	Thickness≥3mm L0=5.65√S0
B650L	≥650	700-880	≥10	≥12	2.0a

B650L steel sheet/plate CEV

Typical designation	CE C,%	CE Carbon equivalent (CE)
B650L	≤0.08	0.29

CE = C + Mn/6 + (Cu + Ni)/15 + (Cr + Mo + V)/5

B650L steel Processing：
Wheel is made up of the rim and the disk. The main processing technique for rim is roll forming. Punch forming and spin forming are usually applied for disc. Punch forming is mainly used for disc of passenger cars, while disc of commercial cars are usually punch-formed (wigh inner tire) or spin-formed (without inner tire).

China special steel limited Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B650L Mechanical and B650L suppliers, we can supply B650L Chemical, B650L Mechanical and B650L standard for you ,please contact us.

Related products : B600L steel , B700L steel

Product

About Us

Manufacture

Name：
Email：
Tel：
Message：