Precipitation-hardening stainless steel UNS S13800
UNS S13800 Equal material : XM-13, 13-8 Mo
UNS S13800 steel is the precipitation of stainless steel, aluminum content is higher, the steel after solid solution treatment the hardness value is not more than 38HRC for cutting. After 510 degree, precipitation hardening, hardness greater than 45HRC, the comprehensive mechanical properties can be obtained strong.
UNS S13800 steel chemical composition:
| Cr | Mo | Ni | N | C | Mn | Si | Al | P | S | |
| Min | 12.3 | 2.00 | 7.5 | 0.35 | ||||||
| Max | 13.2 | 2.50 | 8.5 | 0.01 | 0.05 | 0.20 | 1.0 | 0.95 | 0.010 | 0.008 |
UNS S13800 steel mechanical properties :
Thickness of the steel heat treatment of /mm ó 0.2/MPa ó b/MPa δ (% HRC) hardness 0.10~ < 8 solid solution treatment ≤ 38
0.10~ < 0.50 (510 ± 6) and (510 ± 6) degree precipitation hardening ≥ 1410 ≥ 1515 ≥ 6 ≥ 45
0.50~ < 5 > 8
5.0~8.0 10
UNS S13800 steel physical property:
Solid solution temperature of 1020~1100 degree, water-cooled, hardness ≤ 38HRC.
UNS S13800 steel common product exciting form: UNS S13800 stainless steel plates, UNS S13800 stainless steel sheet, UNS S13800 stainless steel bar, UNS S13800 stainless steel tube.
UNS S13800 stainless steel chief application:
UNS S13800 stainless steel is mainly used in the manufacture of high precision and high wear resistance, corrosion resistant parts.
- Nickle alloys & Super alloys
- Stainless steel & Heat resistant steel
- Carbon steel
- Low alloy high strength steel
- High strength steel
- Boiler steel plate
- Shipbuilding steel plate
- Bridge structural steel
- Weathering steel
- Wear resistant steel
- Pipeline steel
- High carbon steel
- Alloy steel
- CQ/DQ/DDQ/CSS/HSS Grade steel
- Hot rolled steel coil
- Cold rolled steel coil
- Pickled & oiled steel coil
- Electrical steel
- Galvanized and prepainted steel
- Shipbuilding angle steel bar
- Shipbuilding bulb flat bar
- Shipbuilding L shape bars